The Use of Activated Tofu Dregs Waste as an Adsorption Medium for Nitrate Ions
Keywords:
activated carbon, adsorption, nitrate, NaCl, adsorption, nitrate, NaCl, NaCl, Activated Carbon, Adsorption NitrateAbstract
Nitrate ions in water can pose negative impacts on human health, therefore effective and environmentally friendly treatment methods are required. This study aims to evaluate the adsorption capability of NaCl-activated tofu dregs activated carbon for nitrate removal and to determine the optimum adsorption conditions. The activated carbon was prepared through drying, carbonization, and chemical activation using NaCl. The adsorption process was carried out using a nitrate solution with an initial concentration of 150 ppm and a volume of 25 mL, and the nitrate concentration was analyzed using a UV-Vis spectrophotometer at a wavelength of 410 nm. The results showed that the best nitrate adsorption was achieved at an initial nitrate concentration of 350 ppm, a contact time of 60 minutes, an adsorbent mass of 500 mg, and pH 3. These findings indicate that NaCl-activated tofu dregs activated carbon has potential as an alternative adsorbent for nitrate removal from water.
References
Aaltje Manampiring, dr E., & Kes, M. (1964). Studi Kandungan Nitrat (NO-3) Pada Sumber Air Minum Masyarakat Kelurahan Rurukan Kecamatan Tomohon Timur Kota Tomohon.
Ahmed, M. J., Hameed, B. H., & Khan, M. A.
(2023). Recent advances on activated carbon-based materials for nitrate adsorption: A
Review. Journal of Analytical and Applied Pyrolysis, 169(September 2022), 105856.
Https://doi.org/10.1016/j.jaap.2022.105856
Akhir, T., & Hammaam, L. (2024). Sekam padi sebagai natural fiber asdorbent untuk penyerap kandungan pb (ii) dalam air. Ii.
Antika, A., Anita, S., Abu Hanifah, T., Program Kimia, M. S., & Kimia Analitik Jurusan Kimia, B. (2015). potensi arang aktif tulang sapi sebagai adsorben ion timbal, kadmium, nitrat dan klorida dalam larutan. In JOM FMIPA (Vol. 2, Issue 1).
Astuti, R. M. (2017). Analisis proses pembuatan tahu skala rumah dengan Menggunakan pendekatan model Arrhenius.
Universitas Bakrie, 1–28.
Darmokoesoemo, H. (2019). Pengembangan adsorben limbah tahu padat (ltp) terimmobilisasi pada permukaan silika untuk penyisihan berbagai ion logam berat bivalensi dari sampel limbah sintetik.
Dwi Ratna Sari dan Yari Mukti Wibowo, A.(2025). Analisis Kadar Nitrit (NO2¯) dan Nitrat (NO3¯) pada Air Sumur Secara
Spektrofotometer Sinar Tampak. Jurnal Kimia Dan Rekayasa, 5(2), 65–70.152
Eka Putra, S., Juli Puspitasari, D., & Sosidi, H. (2019). Pemanfaatan Karbon Aktif Ampas Tahu Teraktivasi Nacl Sebagai Penyerap Zat Warna Congo Red [The Utilization of Activated Carbon From Tofu Dregs Activated With Sodium Chloride As The Adsorbent Of Congo Red Dye]. KOVALEN:
Jurnal Riset Kimia, 5(1), 109–115. Karbon, K., Teraktivasi, A., Kimia, J., Sains, F.,Maulana, U. I. N., & Ibrahim, M. (2014). DARI AMPAS TAHU Lilik Hartini , Eny Yulianti , Rif ’ atul Mahmudah PENDAHULUAN Ampas tahu merupakan residu yang tertinggal dari proses penyaringan kedelai pada pembuatan tahu (Gao , dkk ., 2013 ). Di jepang ampas tahu dikenal dengan okara . Ampas tahu ya. 3(2).
Mutia Anggraini, T., Fitriani, N., Kunci, K., & Tahu, A. (2018). LIMBAH AMPAS TAHU SEBAGAI BAHAN BAKU UNTUK PRODUKSI BIODIESEL. In Jurnal Integrasi Proses (Vol. 7, Issue 1) Http://jurnal.untirta.ac.id/index.p hp/jip
Ramadha Yanti, D., Oktavia, B., Hamka, J., & Tawar Padang, A. (2022). DESORPSI NITRAT (NO3-) DARI SILIKA GEL TERMODIFIKASI DIMETILAMINA